Gasket Sheet PARO-GAMBIT® type 246
General properties and applications
A high performance sheet, recommended mostly for installations working with steam.
PARO-GAMBIT® is a registered trademark of Gambit Lubawka Sp. z o.o. or its affi liates.
| Material: |
PARO-GAMBIT gasket sheet is based on carbon fi bres, mineral i bres, and fi llers bound with NBR rubber-based binder. |
||
| Designation according to DIN 28091-2: | FA-CM1-O | ||
| ADMISSIONS / CERTIFICATES: | GOST R | ||
| Maximum working conditions: | |||
| Peak temperature | 0C | 450 | |
| Temperature under continuous operation | 0C | -30 - 350 | |
| Temperature under continuous operation with steam | 0C | 350 | |
| Pressure | MPa | 10 | |
| Dimensions: | |||
|
Standard thicknesses of sheets /thicknesses above 5.0 mm are produced by gluing/ |
mm | 0,5; 0,8; 1,0; 1,5; 2,0; 2,5; 3,0; 4,0 |
+/- 0,1 |
|
Standard dimensions of sheets /custom dimensions available within the total range of 1500x3000 mm/ |
mm |
1525x1500 |
+/- 35 |
| Physical and Chemical Properties: | |||
| Density +/- 5 % | g/cm3 | 1,9 | DIN 28090-2 |
| Transverse tensile strength min. | MPa | 10 | DIN 52910 |
| Compressibility | % | 9 - 19 | ASTM F36 |
| Elastic recovery - min. | % | 55 | ASTM F36 |
| Residual stresses 50MPa/16h/300ºC/ (min.) | MPa | 32 | DIN 52913 |
| Residual stresses 50MPa/16h/175ºC/ (min.) | MPa | 35 | DIN 52913 |
| Increase in thickness: | |||
| Oil IRM 903 150oC/5h (max) | % | 12 | ASTM F146 |
| Colour | ginger | ||
The values in the table refer to the gasket sheets with a thickness of 2.0 mm.
All information in this catalogue is based on years of experience in manufacture and use of the discussed products. Since sealing performance in the joint is subject to multiple factors such as mounting method, system parameters, and sealed medium, technical parameters specified herein are of informative nature only and cannot be used as grounds for any claims; any special uses of products are subject to consulting with the manufacturer.