Gasket Sheet Gambit AF-GL®
General properties and applications
Specially selected constituents and structure of AF-GL® gasket sheet ensure high tightness of a joint and resistance to a whole range of media, including steam, water, fuels, oils, solutions of salt as well as weak solutions of acids and bases. Thanks to application of a unique composition of fibres and fillers, gaskets made of this material feature higher resistance to operation in steam.
AF-GL® is a registered trademark of Gambit Lubawka Sp. z o.o. or its affiliates.
| Material: |
Gambit AF – GL® gasket sheet is composed of glass fibres, mineral fibres, Kevlar ® aramid fibres and fillers bound with NBR rubber.
Kevlar® is a registered trademark of E. I. du Pont de Nemours and Company or its affiliates. |
||
| Designation according to DIN 28091-2: | FA-GA1-O | ||
| Approvals/Certificates: | GOST R, DNV GL | ||
| Maximum working conditions: | |||
| Peak temperature | 0C | 400 | |
| Temperature under continuous operation | 0C | -200 - 340 | |
| Temperature under continuous operation with steam | 0C | 250 | |
| Pressure | MPa | 12 | |
| Dimensions: | |||
|
Standard thicknesses of sheets /thicknesses above 5.0 mm are produced by gluing/ |
mm | 0,3; 0,5; 0,8; 1,0; 1,5; 2,0; 2,5; 3,0; 4,0; 5,0 | +/- 0,1 +/- 10% +/- 10% |
|
Standard dimensions of sheets /custom dimensions available within the total range of 1500x3000 mm/ |
mm | 1500x1500 | +/- 10,0 |
| Physical and Chemical Properties: | |||
| Density +/- 5 % | g/cm3 | 1,9 | DIN 28090-2 |
| Transverse tensile strength min. | MPa | 9 | DIN 52910 |
| Compressibility | % | 5 - 15 | ASTM F36 |
| Elastic recovery - min. | % | 55 | ASTM F36 |
| Residual stresses 50MPa/16h/300ºC/ (min.) | MPa | 29 | DIN 52913 |
| Residual stresses 50MPa/16h/175ºC/ (min.) | MPa | 34 | DIN 52913 |
| Increase in thickness: | |||
| Oil IRM 903 150oC/5h (max) | % | 6 | ASTM F146 |
| Model fuel B 200C/5h (max) | % | 6 | ASTM F146 |
| Distilled water 100 °C/4 h max. | % | 2 | ASTM F146 |
| Colour | Steel grey | ||
The values in the table refer to the gasket sheets with a thickness of 2.0 mm.
All information in this catalogue is based on years of experience in manufacture and use of the discussed products. Since sealing performance in the joint is subject to multiple factors such as mounting method, system parameters, and sealed medium, technical parameters specified herein are of informative nature only and cannot be used as grounds for any claims; any special uses of products are subject to consulting with the manufacturer.